Zero Thermal Expansion in ZrMgMo3O12: NMR Crystallography Reveals Origins of Thermoelastic Properties
(American Chemical Society, 2015-03-23)
The coefficient of thermal expansion of ZrMgMo3O12 has been measured and was found to be extremely close to zero over a wide temperature range including room temperature ( = (1.6 ± 0.2) × 10–7 K–1 from 25 to 450 °C by X-ray ...
Mechanical–Structural Investigation of Ion-Exchanged Lithium Silicate Glass using Micro-Raman Spectroscopy
(American Chemical Society, 2016-03-21)
Micro-Raman spectroscopy was used to determine the structural modifications occurring in a simple ion-exchanged glass. The base lithium silicate composition 30Li2O–70SiO2 was studied as it underwent ion exchange, Li+ ↔ K+, ...
Nanoindentation Study of the Surface of Ion-Exchanged Lithium Silicate Glass
(American Chemical Society, 2016-02-25)
Variations in mechanical properties (stiffness and hardness) were measured as a function of case depth in ion-exchange glasses using nanoindentation. A simple silicate composition, 30Li2O–70Si2O, was exchanged (Li+ ↔ K+) ...