NixSi1-x Alloys Prepared by Mechanical Milling as Negative Electrode Materials for Lithium Ion Batteries
Date
2015-10-29Author
Obrovac, MN
Dunlap, R. A.
S.N, Ellis
Du, Zhijia
Metadata
Show full item recordAbstract
NixSi1-x (0 ≤ x ≤ 0.5, x = 0.05) alloys were prepared by ball milling and studied as anode materials for lithium ion batteries. Nanocrystalline Si/NiSi2 phases were formed for x ≤ 0.25. The NiSi phase was observed for samples with higher Ni content. Increasing the Ni content was found to gradually lower the lithiation voltage, while delithiation voltage was not affected for x ≤ 0.25. As a result, Li15Si4 did not form during cycling for x > 0.15. The capacity trend of NixSi1-x alloys with composition suggested that the nanocrystalline NiSi2 phase had some activity toward Li, while the NiSi phase had no capacity toward Li. In situ XRD studies confirmed the activity of nanocrystalline NiSi2. The best cycling performance of NixSi1-x alloys was obtained for x = 0.20 with 94% capacity retention after 50 cycles.
Collections
Rights
CC BY-NC-ND